Cold Vulcanizing Cements

 

 

ADHESIVE TRS 2002 NEW
 
Art. No.   CONTAINER   PACKAGE
302300   1 kg   10 pcs.
302304   5 kg   4 pcs.
302320   240 kg   1 pcs.

Adhesive TRS 2002 NEW is a two-part cold vulcanizing cement based on CR (polychloroprene rubber). Bonds rubber to rubber, rubber to fabric, rubber to metal, fabric to fabric, metal to fabric. The main difference of TRS 2002 NEW cement from TRS 2002 cement is the replacement of trichloroethylene with tetrachloroethylene, a safer organic compound for human organism. Like trichloroethylene, tetrachloroethylene neither ignites nor explodes. TRS 2002 NEW adhesive may be used for works in mines or underground premises.

Use: repair and joining of rubber-fabric conveyor belts, rubber coating of metal surfaces, pulley lagging.

Attention:

TRS 2002 NEW contents methylenechloride and may cause vapor pressure in heat. Avoid hot storage.Cool down to room temperature before use. Open tins,cans or drums carefully when cement was hot!

CHARACTERISTICS   RECOMMENDATIONS
Base: CR - polychloroprene rubber   Working temperature: +15/ +30 ºС
Solvent: tetrachloroethylene, dichloromethane   Hardener: TRS 1000 M
Specific density: 1.45 g/m3   Ratio: 40 g of hardener M per 1 kg of cement
Dynamic viscosity: approx. 3200-3800 mPa·s   Pot life: 1-2 hours
Colour: dark grey   Layer active time: approx. 20 min. at 20°С
Shelf life: 2 years   Application quantity: 300 g/m² per coat
    Vulcanizing time: approx. 24 hours

 

Recommended technology of applying the adhesive mixture on the surfaces to be bonded:

  • rubber/ rubber-cord materials/ fabric: 2 layers;
  • rubber with bonding layer: 1 layer;
  • primed metal: 1 layer.
  Information on TRS 2002 NEW

 

ADHESIVE TRS 4004

 
Art. No.   CONTAINER   PACKAGE
302900   750 ml   10 pcs.
302910   5 l (4,7 kg)   4 pcs.
302905   190 kg   1 pcs.

Adhesive TRS 4004 is a two-part cold vulcanizing cement based on CR (polychloroprene rubber). Binds rubber to rubber, rubber to metal, rubber to fabric, fabric to fabric, metal to fabric. The main difference of TRS 4004 cement is the use of ethyl acetate, a solvent with low toxicity and acceptable odour. It is used for works on open grounds or in well ventilated premises.

Use: repair and joining of rubber-fabric conveyor belts using TRS repair patches, bands and strips, rubber coating of metal surfaces, pulley lagging. Is suitable for repairing and joining of rubber-fabric conveyor belts used in food industry.

CHARACTERISTICS   RECOMMENDATIONS
Base: CR - polychloroprene rubber   Working temperature: +15/ +35 ºС
Solvent: ethyl acetate   Hardener: TRS 1000 E
Specific density: 0.95 g/m3   Ratio: 30 g of hardener per 0.75 kg of cement
Dynamic viscosity: approx. 2800-3200 mPa·s   Pot life: 4-6 hours
Colour: dark grey   Layer active time: approx. 25 min. at 20°С
Shelf life: 2 years   Application quantity: 300 g/m² per coat
    Vulcanizing time: approx. 24 hours

 

Recommended technology of applying the adhesive mixture on the surfaces to be bonded:

  • rubber/ rubber-cord materials/ fabric: 2 layers;
  • rubber with bonding layer: 1 layer;
  • primed metal: 1 layer.
  Information on TRS 4004

 

ADHESIVE TRS 5005

 
Art. No.   CONTAINER   PACKAGE
302920   0,7 kg   10 pcs.
302921   4,7 kg   4 pcs.
302922   190 kg   1 pcs.

Adhesive TRS 5005 is new all-in-one cold vulcanizing cement based on CR (polychloroprene rubber).

Use: joining, rubber coating, lagging and repair.

CHARACTERISTICS   RECOMMENDATIONS
Base: CR - polychloroprene rubber   Working temperature: +15/ +35 ºС
Solvent: butanone (methyl ethyl ketone)   Layer active time: approx. 30 min. at 20°С
Specific density: 0.95 g/m3   Application quantity: 300 g/m² per coat
Dynamic viscosity: approx. 2800-3200 mPa·s   Vulcanizing time: approx. 24 hours
Colour: dark grey    
Shelf life: 3 years    
  Information on TRS 5005

 

ADHESIVE TRS PLASTO

 
Art. No.   CONTAINER   PACKAGE
303110   700 ml   10 pcs.
303111   20 kg   1 pcs.

TRS PLASTO cement is a two-part bonding compound (cement + hardener) for cold or hot bonding. The cement has excellent resistance to acids, oils, ageing and high temperatures.

Use: for bonding PVC, EMPD, PU, ABS, EVA, leather, cork, rubber, nylon, viscose and Kevlar fabrics.

CHARACTERISTICS   RECOMMENDATIONS
Base: PU - polyurethane   Working temperature: +15/ +35 ºС
Solvent: acetone, butanone   Hardener: TRS 1000 E
Specific density: 0.85 g/m3   Ratio: 30 g of hardener per 0.6 kg of cement
Dynamic viscosity: approx. 4000 mPa·s   Pot life: 4-6 hours
Colour: off-white   Layer active time: approx. 5-10 min. at 20°С
Shelf life: 3 years   Application quantity: 300 g/m² per coat
    Vulcanizing time: approx. 6 hours

 

Recommended technology of applying the adhesive mixture on the surfaces to be bonded:

  • 1 layer for each surface.
  Information on TRS PLASTO

 

TRS METAL PRIMER
 
Art. No.   CONTAINER   PACKAGE
307140   700 ml   10 pcs.
307141   170 kg   1 pcs.

TRS METAL PRIMER is used for enhancing the adhesion of rubber to metal. Metal primer used for preparing metal surfaces for applying rubber coatings when using cements TRS 2002, TRS 3003, TRS 4004, TRS 5005.

Use: rubber coating of metal surfaces, pulley lagging.

CHARACTERISTICS   RECOMMENDATIONS
Base: CR - polychloroprene rubber   Working temperature: +15/ +35 ºС
Solvent: phenol, butanone   Drying time: ca. 60 Min. bei 20°С
Specific density: 0.91 g/m3   Application quantity: 300 g/m² per coat
Dynamic viscosity: approx. 500-700 mPa·s   Application: one layer on metal
Colour: black   Shelf life: 3 years

 

  Information on TRS METAL PRIMER

 

HARDENER TRS 1000 M

 
Art. No.   CONTAINER   PACKAGE
302180   40 g   10 pcs.
302220   200 g   6 pcs.

Hardener TRS 1000 М based on Polychloroprene. Not flammable.

Use: hardener for cement TRS 2002, TRS 3003, crosslinking agent for adhesive solutions in footwear industry.

Mixture preparation   TRS 2002   TRS 3003
Cement weight (V)   1 kg   1 kg
Hardener weight   40 g   40 g
Hardener ratio, %   4%   4%

 

  Information on TRS 1000 M

 

HARDENER TRS 1000 E

 
Art. No.   CONTAINER   PACKAGE
700510   30 g   10 pcs.
700511   150 g   6 pcs.

TRS 1000 E hardener is a solution of approx. 29% polyisocyanate in ethyl acetate.

Use: hardener for cement  TRS 4004, TRS PLASTO, crosslinking agent for adhesive solutions in footwear industry.

Mixture preparation   TRS 4004   TRS PLASTO
Cement weight (V)   750 ml   700 ml
Hardener weight   30 g   30 g
Hardener ratio, %   4%   5%

 

  Information on TRS 1000 E

 

HARDENER TRS TRISO
NO PICTURE  
Art. No.   CONTAINER   PACKAGE
         
         

Hardener TRS TRISO is a solution of highly efficient poly-/tri-/isocyanate in ethyl acetate. Excellently adheres to rubber, increases the bond resistance to high temperature, fats, oils, plasticizers, and ensures the adhesion of other hard-to-bond rubber materials.

Use: crosslinking agent for cements based on polyurethane, natural or synthetic rubber.

Mixture preparation   NR   CR   NBR   PU
Base   Natural rubber   Polychloroprene rubber   Nitrile rubber   Polyurethane
TRS TRISO Hardener ratio, %   4-6%   6-8%   6-8%   3-5%

 

  Information on TRS TRISO

 

HARDENER TRS TRISO R
NO PICTURE  
Art. No.   CONTAINER   PACKAGE
         
         

Hardener TRS TRISO R is a solution of highly efficient poly-/tri-/isocyanate in ethyl acetate. The cement solution used ensures high thermal and chemical resistance immediately after bonding. TRS TRISO R adheres to rubber especially well.

Use: crosslinking agent for cements based on chloroprene, polyurethane, natural or synthetic rubber.

Mixture preparation   NR   CR   NBR   PU
Base   Natural rubber   Polychloroprene rubber   Nitrile rubber   Polyurethane
TRS TRISO R Hardener ratio, %   3-6%   4-8%   4-8%   4-7%

 

  Information on TRS TRISO R

 

TRS SOLVENT MEK

 
 
Art. No.   CONTAINER   PACKAGE
304210   0,64 kg   6 pcs.

TRS SOLVENT MEK based on butanone (methyl ethyl ketone).

Use: for degreasing surfaces before bonding, rubber coating, lagging.